MANIFill Micro Hybrid Smart-Shade
MANIFill Micro Hybrid Smart-Shade Composite
MANIFill Micro Hybrid Composite – your premium solution for aesthetic high-class restorations. High translucency to create perfect shades, please also check out our smart shade and incisal shades!
Our intelligent composite with customizable shade. It adapts intelligently to the natural tooth color and thus ensures aesthetically perfect restorations – without the need for time-consuming shade selection. For a natural smile. Fast. Simple. Beautiful.

Product Characteristics
- Highly polishable due to a special particle structure and smooth, homogeneous surface
- Exceptional durability and abrasion resistance
- High plaque resistance due to minimal surface roughness
- Gentle on the gums
- Wide range of shades for advanced aesthetic restorations
Indications
- Class I-V anterior and posterior restorations
- Inlays, onlays, and veneers
- Extended fissure sealing on molars and premolars
- Core build-ups
- Splinting of loosened teeth
- Shape and color corrections to enhance aesthetics

Step by Step
Preparation
- Cleaning of the tooth structure with fluoride-free polishing paste.
- Shade selection in the wet state using the Vita shade guide.
- Prepare the cavity according to the rules of the adhesive technique.
- Ensure that the cavity is dry (rubber dam recommended).
Pulp protection & adhesive system
- Cover deep cavities with calcium hydroxide.
- Etch and bond according to the manufacturer’s instructions.
Composite application
- Apply material from a syringe or cartridge in thin layers (max. 2 mm).
- Model each layer separately.
Curing
- Expose each layer for 20 seconds using a standard dental polymerization unit.
- Hold the light guide as close as possible to the filling surface.
Finishing & polishing
- Finish and polish immediately after polymerization.
- Use finishing diamonds, silicone polishers and polishing brushes.
- Check occlusion and articulation.
Special notes
- Do not place the operating light too close to the material during processing.
- Use a light polymerization unit with a spectrum of 350-500 nm.
Vickers Hardness | 784 MPa |
---|---|
Bending strength | 157 MPa |
E-module | 16575 MPa |
Compressive strength | 432 MPa |
Diametral tensile strength | 56 MPa |
Radiopacity | 220% |
Vol. shrinkage | 1,66% |